ASTM B564 UNS N02200 Nuts, ASTM B564 UNS N02200 Bolts, ASTM B564 UNS N02200 Threaded Rods, ASTM B564 UNS N02200 Studs, ASTM B564 UNS N02200 Screws Supplier in Mumbai, India.
UNS N02200 is the designation for nickel-iron-chromium alloys. UNS N02200 is a nickel-based alloy that can withstand temperatures up to and including 1100°F (593°C). UNS N02200 alloys are used in service temperatures above 1100°F (593°C) when creep and rupture resistance is required, and they are annealed to develop controlled grain size for best characteristics in this temperature range. UNS N02200 is a nickel-iron-chromium-tungsten alloy used in service temperatures above 1100°F (593°C) where creep and rupture resistance is required. It is annealed to achieve optimum qualities in this temperature range.
Chemical Composition
| UNS |
Element |
Composition, % |
| Ni |
Cu |
Fe |
Mn |
C |
Si |
S |
| UNS N02200 |
Ni Alloy |
99.0B min |
0.25 |
0.40 |
0.35 |
0.15 |
0.35 |
0.01 |
Mechanical Properties
| Material and Condition |
Maximum Section Thickness, in. (mm) |
Tensile Strength, min, ksi (MPa) |
Yield Strength, 0.2 % Offset, min, ksi (MPa) |
Elongation in 2 in. or 50 mm or 4D, min, % |
| Nickel alloy UNS N02200, annealed |
... |
55 (380) |
15 (105) |
40 |