ASTM B564 UNS N06022 Bolts, ASTM B564 UNS N06022 Threaded Rods, ASTM B564 UNS N06022 Nuts, ASTM B564 UNS N06022 Screws, ASTM B564 UNS N06022 Studs Supplier in Mumbai, India.
UNS N06022 is the designation for nickel-iron-chromium alloys. UNS N06022 is a nickel-based alloy that can withstand temperatures up to and including 1100°F (593°C). UNS N06022 alloys are used in service temperatures above 1100°F (593°C) when creep and rupture resistance is required, and they are annealed to develop controlled grain size for best characteristics in this temperature range. UNS N06022 is a nickel-iron-chromium-tungsten alloy used in service temperatures above 1100°F (593°C) where creep and rupture resistance is required. It is annealed to achieve optimum qualities in this temperature range.
Chemical Composition
| UNS |
Element |
Composition, % |
| Ni |
Cu |
Fe |
Mn |
C |
Si |
S |
Cr |
Al |
Ti |
Nb + Ta |
Mo |
P |
W |
Co |
V |
| UNS N06022 |
Low C Ni-Mo Cr Alloy |
balanceB |
... |
2.0-6.0 |
0.50 |
0.015 |
0.08 |
0.02 |
20.0-22.5 |
... |
... |
... |
12.5-14.5 |
0.02 |
2.5-3.5 |
2.5 |
0.35 |
Mechanical Properties
| Material and Condition |
Maximum Section Thickness, in. (mm) |
Tensile Strength, min, ksi (MPa) |
Yield Strength, 0.2 % Offset, min, ksi (MPa) |
Elongation in 2 in. or 50 mm or 4D, min, % |
| Low-carbon nickel-chromiummolybdenum alloy UNS N06022, solution annealed |
... |
100 (690) |
45 (310) |
45 |